| Ez. | Erretxina propietateak | Balio tipikoa | Unitatea | Proba metodoa |
| 1 | Grabitate espezifikoa, 23 ℃ | 1.05 | g/cm³ | ASTM D792 |
| 2 | Moldearen uzkurdura, 23℃, 3.2mm, 23℃ | 0,4-0,7 | % | ASTM D955 |
| 3 | Urtze-fluxu-tasa, 220 ℃, 10 kg | 22 | g/10 min | ASTM D1238 |
| 4 | Trakzio-indarra etekinean, 23 ℃, 50 mm/min, 3,2 mm | 49 | MPa | ASTM D638 |
| 5 | Tentsio-luzapena etekinean, 23 ℃, 50 mm/min, 3,2 mm | 5 | %, (Min) | ASTM D638 |
| 6 | Trakzio-luzapena hausturan, 23'℃, 50mm/min, 3.2mm | 10 | %, (Min) | ASTM D638 |
| 7 | Tentsio-modulua, 23 ℃, 50 mm/min, 3,2 mm | 2350 | MPa | ASTM D638 |
| 8 | Flexio-indarra, 23 ℃, 15 mm/min, 3,2 mm | 78 | MPa | ASTM D790 |
| 9 | Flexio-modulua, 23℃, 15mm/min, 3.2mm | 2550 | MPa | ASTM D790 |
| 10 | Izod Inpaktu Indarra, Koskaduna, 3.2mm, 23℃ | 220 | J/m | ASTM D256 |
| 11 | Izod Inpaktu Indarra, Koskaduna, 3.2mm, -30℃ | 90 | J/m | ASTM D256 |
| 12 | Izod Inpaktu Indarra, Koskaduna, 6.4mm, 23℃ | 220 | J/m | ASTM D256 |
| 13 | Izod inpaktu-indarra, koskaduna, 6,4 mm, -30 ℃ | 90 | J/m | ASTM D256 |
| 14 | Rockwell gogortasuna, R eskala | 110 | / | ASTM D785 |
| 15 | HDT, Ertz-noranzkoa, 1.82MPa, 6.4mm, Erregostatu gabea | 85 | °C | ASTM D648 |
| 16 | VICAT, 50N, 50℃/h | 92 | °C | ASTM D1525 |
| 17 | RTI Elektrikoa | 95 | °C | UL 746B |
| 18 | RTI Mekanikoa Inpaktuarekin | 95 | °C | UL 746B |
| 19 | Inpakturik gabeko RTI Mekanikoa | 95 | °C | UL 746B |
| 20 | Sukoitasuna, 1,5 mm | HB | / | UL 94 |
| 21 | Sukoitasuna, 3.0 mm | HB | / | UL 94 |